Reaction product and pigmented basecoat material comprising said product

ABSTRACT

The present invention relates to a pigmented aqueous basecoat material comprising a reaction product which is preparable by reaction of
     (a) at least one aliphatic linear polyester having two functional end groups (a.1),   with   (b) at least one diene polymer having two functional end groups (b.1),   where at least one type of group (a.1) is reacted in a linking manner with at least one type of group (b.1), said components (a) and (b) are used in the reaction in a molar ratio of 2.3/0.7 to 1.7/1.6 and the resulting reaction product possesses a number-average molecular weight of 1000 to 15 000 g/mol.

The present invention relates to innovative pigmented aqueous basecoat materials comprising a specific reaction product. It further relates to the specific new reaction product, and to the use of said reaction product in aqueous basecoat materials. It also relates to a method for producing multicoat paint systems using the new basecoat materials, and also to the multicoat paint systems producible by means of said method.

PRIOR ART

A multiplicity of methods are known for producing multicoat color and/or effect paint systems (also called multicoat coatings or multiple-coat finishes). The prior art discloses (cf., for example, German patent application DE 199 48 004 A1, page 17 line 37 to page 19 line 22, or German patent DE 100 43 405 C1, column 3 paragraph [0018], and column 8 paragraph [0052] to column 9 paragraph [0057], in conjunction with column 6 paragraph [0039] to column 8 paragraph [0050]), for example, the following method in which:

(1) a pigmented aqueous basecoat material is applied to a substrate, (2) a polymer film is formed from the coating material applied in stage (1), (3) a clearcoat material is applied to the resulting basecoat film, and then (4) the basecoat film is cured together with the clearcoat film.

This method is widely employed, for example, for the OEM finishing of automobiles, and also for the painting of metal and plastic ancillary components. The current requirements imposed on the applications-technological and esthetic properties of such paint systems (coatings) are immense.

One problem which arises again and again, and yet has still not been satisfactorily solved by the prior art, is the incidence of what are called pinholes—i.e., the insufficient stability toward pinholes. On successive application of a number of coating materials—basecoat and clearcoat, for example—and in the absence of separate curing of each of the individual polymer films, there may be unwanted inclusions of air, solvent and/or moisture, which may become perceptible in the form of bubbles beneath the surface of the overall paint system, and may break open in the course of the final curing. The holes that are formed in the paint system as a result, also called pinholes, lead to a disadvantageous visual appearance. The amount of organic solvents and/or water obtained as a result of the overall construction of basecoat film and clearcoat film, and also the quantity of air introduced by the application procedure, are too great to be able to escape from the multicoat paint system completely within a final curing step without the generation of defects. The properties of the basecoat material, which is particularly important in this context, and of the coating films produced from it are determined in particular by the binders and additives present in the basecoat material, examples being specific reaction products.

A further factor is that nowadays the replacement of coating materials based on organic solvents by aqueous coating materials is becoming ever more important in order to take account of the rising requirements for environmental friendliness.

Problem

The problem addressed by the present invention, therefore, was that of providing a reaction product and a pigmented aqueous basecoat material which can be used to produce coatings which no longer have the above-identified disadvantages of the prior art. More particularly, the provision of a new reaction product and its use in aqueous basecoat materials ought to make it possible to provide coatings which exhibit outstanding stability toward pinholes and at the same time can be produced by use of aqueous basecoat materials, in an eco-friendly way.

Solution

The stated problems have been solved by a pigmented aqueous basecoat material which comprises a reaction product which is preparable by reaction of

(a) at least one aliphatic linear polyester having two functional end groups (a.1), with (b) at least one diene polymer having two functional end groups (b.1), where at least one type of group (a.1) is reacted in a linking manner with at least one type of group (b.1), said components (a) and (b) are used in the reaction in a molar ratio of 2.3/0.7 to 1.7/1.6 and the resulting reaction product possesses a number-average molecular weight of 1000 to 15 000 g/mol.

The new basecoat material and the new reaction product are also referred to below as basecoat material of the invention and reaction product of the invention. Preferred embodiments are apparent from the description which follows and from the dependent claims.

Likewise provided by the present invention is the use of the reaction product in aqueous basecoat materials for improving the stability toward pinholes. The present invention relates not least to a method for producing a multicoat paint system on a substrate, and also to a multicoat paint system produced by said method.

Through the use of the reaction products of the invention, basecoat materials are obtained whose use in the production of coatings, more particularly multicoat paint systems, leads to outstanding stability toward pinholes. At the same time a high-level environmental profile is ensured. The reaction product of the invention and also the basecoat material of the invention can be used in the OEM finishing sector, particularly in the automobile industry sector, and also in the automotive refinish sector.

Component (a)

The reaction product of the invention is obtainable using at least one aliphatic linear polyester (a) having two functional end groups (a.1).

The types of the functional end groups (a.1) are selected, or harmonized with the types, described later on below, of the functional end groups (b.1) of the diene polymer (b), in such a way that at least one of these types of groups (a.1) can be reacted in a linking reaction with at least one of the types of groups (b.1). The groups (a.1) of a polymer (a) can be the same or different. The same applies to the groups (b.1) of a diene polymer. The groups (b.1) of a diene polymer are preferably identical. The reaction is therefore a linkage of the two components (a) and (b). This linkage may take place under conventional conditions and with conventional mechanisms such as condensation reactions and/or addition reactions. Such types of functional end groups can be selected without problems. The same applies to the combination of these groups, in order to be able to realize linkage of components (a) and (b), by means of appropriate selection, for example, of a nucleophilic functional group (b.1), which is able to attack at an electrophilic center of a functional group (a.1). Examples of functional groups include hydroxyl, carboxyl, amino, thiol, or hydrozide groups. Preferred groups (a.1) are hydroxyl groups and carboxyl groups, since groups of these kinds are present in any case in the form of the reactants when polyesters are prepared. With a special preference the polyester (a) has on average one carboxyl group (a.1) and one hydroxyl group (a.1).

Polyesters as well are known. These are polymeric resins preparable by reaction of polyhydric organic polyols and polybasic organic carboxylic acids (monomers). The polyols and polycarboxylic acids here are linked with one another by esterification, in other words by condensation reactions. Depending on the type, functionality, and fractions and proportions of the starting components that are employed, the products are linear or branched, for example. While linear polymer sections are formed when using difunctional starting components (diols, dicarboxylic acids), branching is achieved for example through the use of alcohols of higher functionality (OH functionality, in other words number of OH groups per molecule, of more than 2). During the preparation it is of course also possible to make proportional use of monofunctional components, examples being monocarboxylic acids. Polyesters can also be prepared, as is known, using the anhydrides of the carboxylic acids, especially the anhydrides of the dicarboxylic acids, instead of or in addition to the corresponding organic carboxylic acids themselves. Likewise possible is preparation through the use of hydroxycarboxylic acids or of the lactones, which are derived from the hydroxycarboxylic acids by intramolecular esterification and are described with more precision later on below.

The term polymer or polymer resin is understood, within the context of the present invention, as follows. A polymer is mixtures of molecules with different sizes. At least a portion of these molecules is distinguished by a sequence of identical or different monomer units (as a reacted form of monomers). A polymer or the corresponding molecule mixture therefore in principle comprises molecules which comprise a plurality of (that is, at least two) identical or different monomer units. It will be appreciated that in the mixture there may also, proportionally, be the monomers themselves, in other words in their unreacted form. This is the reason alone, as is known, for the preparation reaction—that is, in particular, the linkage of monomers—that in general does not proceed with molecular uniformity. Whereas a defined monomer can be assigned a discrete molecular weight, a polymer, therefore, is a mixture of molecules which differ in their molecular weights. A polymer, therefore, cannot be described by a discrete molecular weight, for example, but instead is always assigned average molecular weights such as a number-average molecular weight, for example.

A polymer is therefore considered for the purposes of the present invention to be a mixture of molecules, the mixture comprising molecules which are distinguished by a sequence of identical or different monomer units. On average, then, the molecules making up the polymer embrace in any case more than one monomer or more than one monomer unit. Preferably there are on average at least 3, more particularly at least 5, very preferably at least 7 monomer units present per molecule. The number of monomer units present on average may be determined, for example, by ascertaining the number-average molecular weight and taking account of the molecular weights and proportions of the monomers employed.

The at least one polyester (a) is linear. The expression “linear polyester” means in the context of the present invention that the polymer backbone, in other words the sequence of the ester bonds which make up the linkage of the individual polyester units, has a linear character. The individual compounds (monomers) used for the preparation process therefore possess in each case two functional groups capable of ester bonding, in other words, in particular, hydroxyl groups, carboxyl groups and/or anhydride groups. Linkage then produces a polyester chain or a linear polyester.

The at least one polyester (a) is aliphatic. It is therefore an organic polymer which contains no aromatic groups. This is readily achievable through use of corresponding monomers.

The reactive functional groups (a.1) of the polyester (a) are terminal. This means, therefore, that the functional groups are located in each case at the end of the polyester chain that makes up the linear character.

The number-average molecular weight of the polyester (a) may be, for example, from 200 to 5000 g/mol, especially preferably 500 to 3000 g/mol. Unless specifically indicated otherwise, the number-average molecular weight in the context of the present invention is determined by means of vapor pressure osmosis. Measurement was carried out in the context of the present invention by means of a vapor pressure osmometer (model 10.00 from Knauer) on concentration series of the component under investigation in toluene at 50° C., with benzophenone as calibration substance for determination of the experimental calibration constant of the instrument employed (in accordance with E. Schroder, G. Müller, K.-F. Arndt, “Leitfaden der Polymercharakterisierung” [Introduction to polymer characterization], Akademie-Verlag, Berlin, pp. 47-54, 1982, in which benzil was used as calibration substance).

The reaction product of the invention is preparable using the described polyesters (a). This does not, however, mean necessarily that the component in question must also necessarily be employed.

Not only possible but in fact preferred in the context of the present invention is for the reaction product of the invention to be prepared by ring-opening reaction of an aliphatic lactone with a diene polymer having two hydroxyl end groups as described later on below.

As is known, ring-opening polymerization of lactones produces polyesters. Employed generally in this case as starter or catalyst are organic alcohols. The hydroxyl group of the alcohols attacks nucleophilically at the intramolecular ester group of a lactone molecule. An ester linkage is produced between starter alcohol and the lactone molecule. As a result of the ring opening, the latter molecule has a further reactive OH group (or the correspondingly deprotonated group), which is able to attack at a further lactone molecule in the manner described. Ring-opening reaction of an aliphatic lactone with a diene polymer as described later on below therefore means that the diene polymer is used as starter and then the lactone is reacted successively in the manner described to form an aliphatic polyester attached to the diene polymer. This means formally, then, that the molecules of the polyester (a) possess one carboxyl group and one hydroxyl group (a.1) as groups (a.1). In this case, the molecules of the diene polymer possess two hydroxyl groups as groups (b.1). The linking reaction in this case is then between the carboxyl groups (a.1) of the polyester (a) and the hydroxyl groups (b.1) of the diene polymer (b). Accordingly, one type of groups (a.1) (viz. the carboxyl groups) is reacted with one type of groups (b.1) (viz. hydroxyl groups) present, in a linking reaction. The reaction product then has free hydroxyl end groups, which in particular are the hydroxyl groups (a.1) of the polyester (a).

Where reference is made in the context of the present invention to the reaction of the groups or types of groups, the reaction in question may be either a proportional or else a complete reaction of the groups present. For reasons simply of experimental statistics, however, even in the case where the aim is for a complete reaction, such ideal complete reaction is generally not achieved.

Aliphatic lactones are known. They are heterocyclic organic compounds which have an ester bond within the molecule ring. Ultimately, then, they are intramolecular esters of hydroxycarboxylic acids. The aliphatic lactones known per se may be used, examples being gamma-valerolactone or epsilon-caprolactone.

The aliphatic lactones therefore have a heterocyclic structure; preferred lactones may be described by the following structural formula (I):

in which R₁, R₂, R₃, and R₄, independently of one another, are H, C₁ to C₆ alkyl, C₃ to C₆ alkylene, or C₁ to C₆ alkoxy, preferably H or C₁ to C₄ alkyl, more particularly H, and n and m, independently of one another, are an integer from 0 to 6, preferably 1 to 4, and n+m is preferably 2 to 6, especially preferably 2 to 4, more preferably 3.

Preferred lactones are beta-propiolactone, gamma-butyrolactone, gamma-valerolactone, epsilon-caprolactone, or methyl-epsilon-caprolactone, preferably gamma-butyrolactone and epsilon-caprolactone, very preferably epsilon-caprolactone. Such lactones (a) may be obtained commercially.

Component (b)

The reaction products of the invention may be prepared using at least one diene polymer having two functional end groups (b.1).

The groups (b.1) or the types of groups (b.1) are subject correspondingly to the comments in the description above for the groups (a.1) or the types of groups (a.1). Mention may by way of example be made of hydroxyl, carboxyl, amino, thiol, and hydrazide groups. Where carboxyl groups are selected as groups (a.1), examples of groups (b.1) selected are hydroxyl and/or amino groups, preferably hydroxyl groups, since these groups react with carboxyl groups under customary conditions. A similar situation applies if the preferred ring-opening reaction is carried out with an aliphatic lactone. This is because the reaction with the lactone corresponds formally to a reaction of a hydroxyl group (b.1) with a carboxyl group (a.1). Formally this means that the polyester (a) contains on average one carboxyl group (a.1) and one hydroxyl group (a.1), while the diene polymer has two hydroxyl groups (b.1). The functional group (a.1) which is linkingly reacted with a hydroxyl group (b.1) is then the carboxyl group.

Groups reactive with one another (groups which are linkingly reacted) are therefore considered in particular to be the following pairings: hydroxyl groups with carboxylic acid groups, and amino groups with carboxylic acid groups. Preference is given to the linking reaction of hydroxyl groups with carboxylic acid groups to from an ester bond.

Diene polymers having two functional end groups such as hydroxyl or amino groups are known. Diene polymers generally are polymers prepared by polymerization of conjugated diene monomers having in particular 4 to 8 carbon atoms such as preferably butadiene, isoprene, or dimethylbutadiene. The polymerization may take place via various mechanisms known per se, using known polymerization initiators, more particularly by radical or anionic polymerization mechanisms. Functional end groups are introduced readily via the use of specific initiators, by means of which the functional groups or precursors of these groups may be introduced, and/or by the deliberate termination of initially prepared diene polymers with compounds through which the functional groups may be introduced. An example is the termination of polybutadienes with alkylene oxides such as ethylene oxide or propylene oxide, leading to hydroxyl-terminated polybutadienes. Typical number-average molecular weights of such diene polymers are from, for example, 200 to 10 000 g/mol. The preparation of such diene polymers has been described in many instances, with reference being made for example to EP 1 439 194 A1, EP 0 058 329 B1, DE 2 900 880 A1, DE 2 908 298 A1, or else EP 1 314 744 A2. Such diene polymers are obtainable commercially.

Preferred in the context of the present invention are polybutadienes. Polybutadienes are known, being polymers of 1,3-butadiene. Their preparation, which proceeds generally via an anionic polymerization, may lead to 1,4 linkages (the resulting base units of the polymer backbone comprising an olefinically unsaturated bond which may be in cis or trans configuration) and 1,2 linkages (the olefinically unsaturated bond is located in the side chain). Depending on the catalyst and reaction conditions employed, the polybutadienes may comprise varying proportions of 1,4-cis, 1,4-trans, and 1,2 linkages (determination possible by, for example, infrared and/or NMR spectroscopy). The types of catalysts which can be employed and the types of possible reaction regimes are known. Also possible is for the polybutadienes to be hydrogenated after preparation, in other words for the double bonds to be proportionally or completely hydrogenated. Hydrogenated polybutadienes of this kind are also known.

The polybutadienes possess for example a number-average molecular weight of 200 to 10 000 g/mol, preferably 500 to 5000 g/mol, especially preferably 750 to 3000 g/mol. Such polybutadienes are available, for example, under the trade names Krasol or Poly bd (from Cray Valley), and can be used directly for preparing the reaction products.

The Reaction Product

The preparation of the reaction product of the invention via components (a) and (b) may take place in accordance with common-knowledge methods. Here, both components are linked to one another via likewise common-knowledge condensation and/or addition reactions. Accordingly, at least one type of group (a.1) of component (a) is reacted with at least one type of group (b.1) of component (b). Which groups can be linkingly reacted with one another is known and has also already been elucidated earlier on above. Preferred combinations are the following: hydroxyl group with carboxyl group, amino group with carboxyl group, amino group with isocyanate group.

It is preferred for carboxyl groups (a.1) of component (a) to be linkingly reacted with hydroxyl groups (b.1) of component (b). A reaction of this kind may take place, for example, in bulk or in solution with typical organic solvents at temperatures from, for example, 50° C. to 300° C. It is of course also possible for typical catalysts to be employed, such as sulfuric acid, sulfonic acids and/or tetraalkyl titanates, zinc and/or tin alkoxylates, dialkyltin oxides such as di-n-butyltin oxide, for example, or organic salts of the dialkyltin oxides. Customarily, at least in the case of condensation reactions, a water separator is also used, in order to collect the water formed.

The components (a) and (b) are used in the possible preparation in a molar ratio of 2.3/0.7 to 1.7/1.6, preferably 2.2/0.8 to 1.8/1.6, and very preferably of 2.1/0.9 to 1.8/1.5. Even more preferred is a ratio of 2.1/0.9 to 1.8/1.0. Especially preferred is a ratio of 2.0/1.0. At any rate, therefore, component (a) is used in a molar excess.

In the preferred case in which the reaction product of the invention is prepared by ring-opening reaction of an aliphatic lactone with a diene polymer containing two hydroxyl end groups, preferably a polybutadiene, the following applies. Since in this case the polyester (a) is prepared practically in situ, thus meaning that the preparation of the polyester (a) is inseparably connected with the preferably two-sided attachment to the diene polymer, the result on average is a reaction product in which a centrally located diene polymer is linked, preferably via two ester bonds, to two terminal polyester units. In this preferred case, then, in formal terms, the ratio of the components (a) and (b) is 2.0/1.0. The molecular weight of the aliphatic linear polyester and hence also of the resulting reaction product can then be adjusted easily through the choice of the stochiometric ratio of lactone employed to diene polymer. Where, for example, one equivalent of diene polymer is reacted with ten equivalents of lactone, the reaction product on average has the form A-B-A, where A is a polyester segment consisting on average of five lactone units, and B is a diene polymer segment. This will be reflected, within experimental error limits, in the number-average molecular weight of the reaction product that is subsequently determined experimentally. In this embodiment, the molar ratio of aliphatic lactone to diene polymer is 2/1 to 50/1, preferably 5/1 to 40/1, especially preferably 10/1 to 30/1. From a ratio of at least 5/1 upward in particular, it can be guaranteed, purely on a statistical basis, that the product has a polyester segment on both sides of the diene polymer.

The reaction product of the invention preferably possesses only a low acid number of less than 10 mg KOH/g. It preferably possesses an acid number of less than 7.5 mg KOH/g and very preferably of less than 5 mg KOH/g. The acid number is determined in accordance with DIN 53402. If reference is made in the context of the present invention to an official standard, this of course means the version of the standard that was current on the filing date, or, if no current version exists at that date, then the last current version.

The reaction product of the invention possesses a number-average molecular weight of 1000 to 15 000 g/mol, preferably 1200 to 10 000 g/mol and very preferably 1500 to 5000 g/mol.

The reaction product of the invention is generally hydroxy-functional, preferably on average dihydroxy-functional.

Particularly preferred embodiments are specified below:

a) In one particularly preferred embodiment of the reaction product of the invention, it is prepared by ring-opening reaction of an aliphatic lactone, preferably epsilon-caprolactone, with a diene polymer containing two hydroxyl end groups, preferably a polybutadiene, with the molar ratio of aliphatic lactone and diene polymer being from 2/1 to 50/1, more particularly 5/1 to 40/1. b) In another particularly preferred embodiment of the reaction product of the invention, the diene polymer, preferably the polybutadiene possesses a number-average molecular weight of 500 to 5000 g/mol. c) In another particularly preferred embodiment of the reaction product of the invention, said product possesses an acid number of less than 10 mg KOH/g. d) In another particularly preferred embodiment of the reaction product of the invention, said product possesses a number-average molecular weight of 1500 to 5000 g/mol.

In one especially preferred embodiment of the reaction product of the invention, all of the features indicated under a) to d) are realized in combination.

The Pigmented Aqueous Basecoat Material

The present invention further relates to a pigmented aqueous basecoat material which comprises at least one reaction product of the invention. All of the preferred embodiments stated above with regard to the reaction product also, of course, apply in respect of the basecoat material comprising the reaction product.

A basecoat material is a color-imparting intermediate coating material that is used in automotive finishing and general industrial painting. This basecoat material is generally applied to a metallic or plastics substrate which has been pretreated with a baked (fully cured) surfacer or primer-surfacer, or else, occasionally, is applied directly to the plastics substrate. Substrates used may also include existing paint systems, which may optionally require pretreatment as well (by abrading, for example). It has now become entirely customary to apply more than one basecoat film. Accordingly, in such a case, a first basecoat film constitutes the substrate for a second such film. A particular possibility in this context, instead of application to a coat of a baked surfacer, is to apply the first basecoat material directly to a metal substrate provided with a cured electrocoat, and to apply the second basecoat material directly to the first basecoat film, without separately curing the latter. To protect a basecoat film, or the uppermost basecoat film, from environmental effects in particular, at least an additional clearcoat film is applied over it. This is generally done in a wet-on-wet process—that is, the clearcoat material is applied without the basecoat film being cured. Curing then takes place, finally, jointly. It is now also widespread practice to produce only one basecoat film on a cured electrocoat film, then to apply a clearcoat material, and then to cure these two films jointly.

The sum total of the weight-percentage fractions, based on the total weight of the pigmented aqueous basecoat material, of all reaction products of the invention is preferably 0.1 to 30 wt %, more preferably 1 to 20 wt %, and very preferably 1.5 to 15 wt % or even 2 to 12 wt %.

Where the amount of the reaction product of the invention is below 0.1 wt %, it may be possible that no further improvement in stability with respect to pinholes is achieved. Where the amount is more than 30 wt %, there may in certain circumstances be disadvantages, such as incompatibility of said reaction product in the basecoat material, for example. Such incompatibility may be manifested, for example, in uneven leveling and also in floating or settling.

In the case of a possible particularization to basecoat materials comprising preferred reaction products in a specific proportional range, the following applies. The reaction products which do not fall within the preferred group may of course still be present in the basecoat material. In that case the specific proportional range applies only to the preferred group of reaction products. It is preferred nonetheless for the total proportion of reaction products, consisting of reaction products of the preferred group and reaction products which are not part of the preferred group, to be subject likewise to the specific proportional range.

In the case of restriction to a proportional range of 1.5 to 15 wt % and to a preferred group of reaction products, therefore, this proportional range evidently applies initially only to the preferred group of reaction products. In that case, however, it would be preferable for there to be likewise from 1.5 to 15 wt % in total present of all originally encompassed reaction products, consisting of reaction products from the preferred group and reaction products which do not form part of the preferred group. If, therefore, 5 wt % of reaction products of the preferred group are used, not more than 10 wt % of the reaction products of the nonpreferred group may be used.

The stated principle is valid, for the purposes of the present invention, for all stated components of the basecoat material and for their proportional ranges—for example, for the pigments, for the polyurethane resins as binders, or else for the crosslinking agents such as melamine resins.

The basecoat materials used in accordance with the invention comprise color and/or effect pigments. Such color pigments and effect pigments are known to those skilled in the art and are described, for example, in Rompp-Lexikon Lacke and Druckfarben, Georg Thieme Verlag, Stuttgart, New York, 1998, pages 176 and 451. The fraction of the pigments may be situated for example in the range from 1 to 40 wt %, preferably 2 to 30 wt %, more preferably 3 to 25 wt %, based on the total weight of the pigmented aqueous basecoat material. Preferred basecoat materials in the context of the present invention are those which comprise, as binders, polymers curable physically, thermally, or both thermally and with actinic radiation. A “binder” in the context of the present invention and in accordance with relevant DIN EN ISO 4618 is the nonvolatile component of a coating composition, without pigments and fillers. Specific binders, accordingly, include, for example, typical coatings additives, the reaction product of the invention, or typical crosslinking agents described later on below, even if the expression is used primarily below in relation to particular polymers curable physically, thermally, or both thermally and with actinic radiation, as for example particular polyurethane resins.

Besides the reaction product of the invention, the pigmented aqueous basecoat materials of the invention more preferably comprise at least one polyurethane resin as binder. Coating materials of this kind comprising polyurethane resins may likewise customarily be cured physically, thermally, or both thermally and with actinic radiation.

In the context of the present invention, the term “physical curing” means the formation of a film through loss of solvent from polymer solutions or polymer dispersions. Typically, no crosslinking agents are necessary for this curing.

In the context of the present invention, the term “thermal curing” means the heat-initiated crosslinking of a coating film, with either a separate crosslinking agent or else self-crosslinking binders being employed in the parent coating material. The crosslinking agent contains reactive functional groups which are complementary to the reactive functional groups present in the binders. This is commonly referred to by those in the art as external crosslinking. Where the complementary reactive functional groups or autoreactive functional groups—that is, groups which react with groups of the same kind—are already present in the binder molecules, the binders present are self-crosslinking. Examples of suitable complementary reactive functional groups and autoreactive functional groups are known from German patent application DE 199 30 665 A1, page 7 line 28 to page 9 line 24.

For the purposes of the present invention, actinic radiation means electromagnetic radiation such as near infrared (NIR), UV radiation, more particularly UV radiation, and particulate radiation such as electron radiation. Curing by UV radiation is commonly initiated by radical or cationic photoinitiators. Where thermal curing and curing with actinic light are employed in unison, the term “dual cure” is also used.

In the present invention preference is given both to basecoat materials which cure physically and to basecoat materials which cure thermally or both thermally and with actinic radiation, i.e., by “dual cure”.

Preferred thermally curing basecoat materials are those which comprise as binder a polyurethane resin, preferably a hydroxyl-containing polyurethane resin, and as crosslinking agent an aminoplast resin or a blocked or nonblocked polyisocyanate, preferably an aminoplast resin. Among the aminoplast resins, melamine resins are preferred.

The sum total of the weight-percentage fractions, based on the total weight of the pigmented aqueous basecoat material, of all crosslinking agents, preferably aminoplast resins and/or blocked and/or nonblocked polyisocyanates, more particularly preferably melamine resins, is preferably 1 to 20 wt %, more preferably 1.5 to 17.5 wt %, and very preferably 2 to 15 wt % or even 2.5 to 10 wt %.

The polyurethane resin preferably present may be ionically and/or nonionically hydrophilically stabilized. In preferred embodiments of the present invention the polyurethane resin is ionically hydrophilically stabilized. The preferred polyurethane resins are linear or contain instances of branching. The polyurethane resin is more preferably one in whose presence olefinically unsaturated monomers have been polymerized. This polyurethane resin may be present alongside the polymer originating from the polymerization of the olefinically unsaturated monomers, without these polymers being bonded covalently to one another. Equally, however, the polyurethane resin may also be bonded covalently to the polymer originating from the polymerization of the olefinically unsaturated monomers. The olefinically unsaturated monomers are preferably monomers containing acrylate groups and/or methacrylate groups. It is likewise preferred for the monomers containing acrylate and/or methacrylate groups to be used in combination with other olefinically unsaturated compounds which contain no acrylate or methacrylate groups. Olefinically unsaturated monomers attached to the polyurethane resin are more preferably monomers containing acrylate groups or methacrylate groups, thereby producing polyurethane (meth)acrylates. Very preferably the polyurethane resin is a polyurethane (meth)acrylate. The polyurethane resin present with preference is curable physically, thermally, or both thermally and with actinic radiation. More particularly it is curable either thermally or both thermally and with actinic radiation. With particular preference the polyurethane resin comprises reactive functional groups through which external crosslinking is possible.

Suitable saturated or unsaturated polyurethane resins are described, for example, in

-   -   German patent application DE 199 14 896 A1, column 1, lines 29         to 49 and column 4, line 23 to column 11, line 5,     -   German patent application DE 199 48 004 A1, page 4, line 19 to         page 13, line 48,     -   European patent application EP 0 228 003 A1, page 3, line 24 to         page 5, line 40,     -   European patent application EP 0 634 431 A1, page 3, line 38 to         page 8, line 9, or     -   international patent application WO 92/15405, page 2, line 35 to         page 10, line 32.

The polyurethane resin is prepared using preferably the aliphatic, cycloaliphatic, aliphatic-cycloaliphatic, aromatic, aliphatic-aromatic and/or cycloaliphatic-aromatic polyisocyanates that are known to the skilled person.

As alcohol component for preparing the polyurethane resins, preference is given to using the saturated and unsaturated polyols of relatively high molecular mass and of low molecular mass, and also, optionally, monoalcohols, in minor amounts, that are known to the skilled person. Low molecular mass polyols used are more particularly diols and, in minor amounts, triols, for introducing instances of branching. Examples of suitable polyols of relatively high molecular mass are saturated or olefinically unsaturated polyester polyols and/or polyether polyols. Relatively high molecular mass polyols are more particularly polyester polyols, especially those having a number-average molecular weight of 400 to 5000 g/mol.

For hydrophilic stabilization and/or for increasing the dispersibility in aqueous medium, the polyurethane resin preferably present may contain particular ionic groups and/or groups which can be converted into ionic groups (potentially ionic groups). Polyurethane resins of this kind are referred to in the context of the present invention as ionically hydrophilically stabilized polyurethane resins. Likewise present may be nonionic hydrophilically modifying groups. Preferred, however, are the ionically hydrophilically stabilized polyurethanes. In more precise terms, the modifying groups are alternatively

-   -   functional groups which can be converted to cations by         neutralizing agents and/or quaternizing agents, and/or cationic         groups (cationic modification) or     -   functional groups which can be converted to anions by         neutralizing agents, and/or anionic groups (anionic         modification) and/or     -   nonionic hydrophilic groups (nonionic modification).

As the skilled person is aware, the functional groups for cationic modification are, for example, primary, secondary and/or tertiary amino groups, secondary sulfide groups and/or tertiary phosphine groups, more particularly tertiary amino groups and secondary sulfide groups (functional groups which can be converted to cationic groups by neutralizing agents and/or quaternizing agents). Mention should also be made of the cationic groups—groups prepared from the aforementioned functional groups using neutralizing agents and/or quaternizing agents known to those skilled in the art—such as primary, secondary, tertiary and/or quaternary ammonium groups, tertiary sulfonium groups and/or quaternary phosphonium groups, more particularly quaternary ammonium groups and tertiary sulfonium groups.

As is well known, the functional groups for anionic modification are, for example, carboxylic acid, sulfonic acid and/or phosphonic acid groups, more particularly carboxylic acid groups (functional groups which can be converted to anionic groups by neutralizing agents), and also anionic groups—groups prepared from the aforementioned functional groups using neutralizing agents known to the skilled person—such as carboxylate, sulfonate and/or phosphonate groups.

The functional groups for nonionic hydrophilic modification are preferably poly(oxyalkylene) groups, more particularly poly(oxyethylene) groups.

The ionically hydrophilic modifications can be introduced into the polyurethane resin through monomers which contain the (potentially) ionic groups. The nonionic modifications are introduced, for example, through the incorporation of poly(ethylene) oxide polymers as lateral or terminal groups in the polyurethane molecules. The hydrophilic modifications are introduced, for example, via compounds which contain at least one group reactive toward isocyanate groups, preferably at least one hydroxyl group. The ionic modification can be introduced using monomers which, as well as the modifying groups, contain at least one hydroxyl group. To introduce the nonionic modifications, preference is given to using the polyether diols and/or alkoxypoly(oxyalkylene) alcohols known to those skilled in the art.

The polyurethane resin may preferably be a graft polymer. More particularly it is a polyurethane resin grafted with olefinically unsaturated compounds, preferably olefinically unsaturated monomers. In this case, then, the polyurethane is grafted, for example, with side groups and/or side chains that are based on olefinically unsaturated monomers. These are more particularly side chains based on poly(meth)acrylates. Poly(meth)acrylates for the purposes of the present invention are polymers or polymeric radicals which comprise monomers containing acrylate and/or methacrylate groups, and preferably consist of monomers containing acrylate groups and/or methacrylate groups. Side chains based on poly(meth)acrylates are understood to be side chains which are constructed during the graft polymerization, using monomers containing (meth)acrylate groups. In the graft polymerization, preference here is given to using more than 50 mol %, more particularly more than 75 mol %, especially 100 mol %, based on the total amount of the monomers used in the graft polymerization, of monomers containing (meth)acrylate groups.

The side chains described are introduced into the polymer preferably after the preparation of a primary polyurethane resin dispersion. In this case the polyurethane resin present in the primary dispersion may contain lateral and/or terminal olefinically unsaturated groups via which, then, the graft polymerization with the olefinically unsaturated compounds proceeds. The polyurethane resin for grafting may therefore be an unsaturated polyurethane resin (A). The graft polymerization is in that case a radical polymerization of olefinically unsaturated reactants. Also possible, for example, is for the olefinically unsaturated compounds used for the graft polymerization to contain at least one hydroxyl group. In that case it is also possible first for there to be attachment of the olefinically unsaturated compounds via these hydroxyl groups through reaction with free isocyanate groups of the polyurethane resin. This attachment takes place instead of or in addition to the radical reaction of the olefinically unsaturated compounds with the lateral and/or terminal olefinically unsaturated groups optionally present in the polyurethane resin. This is then followed again by the graft polymerization via radical polymerization, as described earlier on above. The result in any case is polyurethane resins grafted with olefinically unsaturated compounds, preferably olefinically unsaturated monomers.

As olefinically unsaturated compounds with which the polyurethane resin (A) is preferably grafted it is possible to use virtually all radically polymerizable, olefinically unsaturated, and organic monomers which are available to the skilled person for these purposes. A number of preferred monomer classes may be specified by way of example:

-   -   hydroxyalkyl esters of (meth)acrylic acid or of other         alpha,beta-ethylenically unsaturated carboxylic acids,     -   (meth)acrylic acid alkyl and/or cycloalkyl esters having up to         20 carbon atoms in the alkyl radical,     -   ethylenically unsaturated monomers comprising at least one acid         group, more particularly exactly one carboxyl group, such as         (meth)acrylic acid, for example,     -   vinyl esters of monocarboxylic acids which are branched in         alpha-position and have 5 to 18 carbon atoms,     -   reaction products of (meth)acrylic acid with the glycidyl ester         of a monocarboxylic acid which is branched in alpha-position and         has 5 to 18 carbon atoms,     -   further ethylenically unsaturated monomers such as olefins         (ethylene for example), (meth)acrylamides, vinylaromatic         hydrocarbons (styrene for example), vinyl compounds such as         vinyl chloride and/or vinyl ethers such as ethyl vinyl ether.

Used with preference are monomers containing (meth)acrylate groups, and so the side chains attached by grafting are poly(meth)acrylate-based side chains.

The lateral and/or terminal olefinically unsaturated groups in the polyurethane resin, via which the graft polymerization with the olefinically unsaturated compounds can proceed, are introduced into the polyurethane resin preferably via particular monomers. These particular monomers, in addition to an olefinically unsaturated group, also include, for example, at least one group that is reactive toward isocyanate groups. Preferred are hydroxyl groups and also primary and secondary amino groups. Especially preferred are hydroxyl groups.

The monomers described through which the lateral and/or terminal olefinically unsaturated groups may be introduced into the polyurethane resin may also, of course, be employed without the polyurethane resin being additionally grafted thereafter with olefinically unsaturated compounds. It is preferred, however, for the polyurethane resin to be grafted with olefinically unsaturated compounds.

The polyurethane resin preferably present may be a self-crosslinking and/or externally crosslinking binder. The polyurethane resin preferably comprises reactive functional groups through which external crosslinking is possible. In that case there is preferably at least one crosslinking agent in the pigmented aqueous basecoat material. The reactive functional groups through which external crosslinking is possible are more particularly hydroxyl groups. With particular advantage it is possible, for the purposes of the method of the invention, to use polyhydroxy-functional polyurethane resins. This means that the polyurethane resin contains on average more than one hydroxyl group per molecule.

The polyurethane resin is prepared by the customary methods of polymer chemistry. This means, for example, the polymerization of polyisocyanates and polyols to polyurethanes, and the graft polymerization that preferably then follows with olefinically unsaturated compounds. These methods are known to the skilled person and can be adapted individually. Exemplary preparation processes and reaction conditions can be found in European patent EP 0521 928 B1, page 2, line 57 to page 8, line 16.

The polyurethane resin preferably present preferably possesses a number-average molecular weight of 200 to 30 000 g/mol, more preferably of 2000 to 20 000 g/mol. It further possesses, for example, a hydroxyl number of to 250 mg KOH/g, but more particularly from 20 to 150 mg KOH/g. The acid number of the polyurethane resin is preferably 5 to 200 mg KOH/g, more particularly 10 to 40 mg KOH/g. The hydroxyl number is determined in the context of the present invention in accordance with DIN 53240, the acid number in accordance with DIN 53402.

The polyurethane resin content is preferably between 5 and 80 wt %, more preferably between 8 and 70 wt %, and very preferably between 10 and 60 wt %, based in each case on the film-forming solids of the basecoat material.

By film-forming solids, corresponding ultimately to the binder fraction, is meant the nonvolatile weight fraction of the basecoat material, without pigments and, where appropriate, fillers. The film-forming solids can be determined as follows: A sample of the pigmented aqueous basecoat material (approximately 1 g) is admixed with 50 to 100 times the amount of tetrahydrofuran and then stirred for around 10 minutes. The insoluble pigments and any fillers are then removed by filtration and the residue is rinsed with a little THF, the THF being removed from the resulting filtrate on a rotary evaporator. The residue of the filtrate is dried at 120° C. for two hours and the resulting film-forming solids are obtained by weighing.

The sum total of the weight-percentage fractions, based on the total weight of the pigmented aqueous basecoat material, of all polyurethane resins is preferably 2 to 40 wt %, more preferably 2.5 to 30 wt %, and very preferably 3 to 20 wt %.

The pigmented aqueous basecoat material to be used may further comprise at least one polyester different from the reaction products of the invention, more particularly a polyester having a number-average molecular weight of 400 to 5000 g/mol, as binder. Such polyesters are described for example in DE 4009858 in column 6, line 53 to column 7, line 61 and column 10, line 24 to column 13, line 3.

There is preferably also a thickener present. Suitable thickeners are inorganic thickeners from the group of the sheet silicates. As well as the inorganic thickeners, however, it is also possible to use one or more organic thickeners. These are preferably selected from the group consisting of (meth)acrylic acid-(meth)acrylate copolymer thickeners, for example the commercial product Rheovis AS S130 (BASF), and of polyurethane thickeners, for example the commercial product Rheovis PU 1250 (BASF). The thickeners used are different from the binders used.

Furthermore, the pigmented aqueous basecoat material may further comprise at least one adjuvant. Examples of such adjuvants are salts which can be decomposed thermally without residue or substantially without residue, resins as binders that are curable physically, thermally and/or with actinic radiation and are different from polyurethane resins, further crosslinking agents, organic solvents, reactive diluents, transparent pigments, fillers, molecularly dispersely soluble dyes, nanoparticles, light stabilizers, antioxidants, deaerating agents, emulsifiers, slip additives, polymerization inhibitors, initiators of radical polymerizations, adhesion promoters, flow control agents, film-forming assistants, sag control agents (SCAs), flame retardants, corrosion inhibitors, waxes, siccatives, biocides, and flatting agents.

Suitable adjuvants of the aforementioned kind are known, for example, from

-   -   German patent application DE 199 48 004 A1, page 14, line 4, to         page 17, line 5,     -   German patent DE 100 43 405 C1 column 5, paragraphs [0031] to         [0033].

They are used in the customary and known amounts.

The solids content of the basecoat materials of the invention may vary according to the requirements of the case in hand. The solids content is guided primarily by the viscosity required for application, more particularly for spray application, and so may be adjusted by the skilled person on the basis of his or her general art knowledge, optionally with assistance from a few exploratory tests.

The solids content of the basecoat materials is preferably 5 to 70 wt %, more preferably 8 to 60 wt %, and very preferably 12 to 55 wt %.

By solids content (nonvolatile fraction) is meant that weight fraction which remains as a residue on evaporation under specified conditions. In the present application, the solids content, unless explicitly indicated otherwise, is determined in accordance with DIN EN ISO 3251. This is done by evaporating the basecoat material at 130° C. for 60 minutes.

Unless indicated otherwise, this test method is likewise employed in order to determine, for example, the fraction of various components of the basecoat material as a proportion of the total weight of the basecoat material. Thus, for example, the solids of a dispersion of a polyurethane resin which is to be added to the basecoat material may be determined correspondingly in order to ascertain the fraction of this polyurethane resin as a proportion of the overall composition.

The basecoat material of the invention is aqueous. The expression “aqueous” is known in this context to the skilled person. The phrase refers in principle to a basecoat material which is not based exclusively on organic solvents, i.e., does not contain exclusively organic-based solvents as its solvents but instead, in contrast, includes a significant fraction of water as solvent. “Aqueous” for the purposes of the present invention should preferably be understood to mean that the coating composition in question, more particularly the basecoat material, has a water fraction of at least 40 wt %, preferably at least 50 wt %, very preferably at least 60 wt %, based in each case on the total amount of the solvents present (i.e., water and organic solvents). Preferably in turn, the water fraction is 40 to 90 wt %, more particularly 50 to 80 wt %, very preferably 60 to 75 wt %, based in each case on the total amount of the solvents present.

The basecoat materials employed in accordance with the invention may be produced using the mixing assemblies and mixing techniques that are customary and known for producing basecoat materials.

The Method of the Invention and the Multicoat Paint System of the Invention

A further aspect of the present invention is a method for producing a multicoat paint system, where

(1) a pigmented aqueous basecoat material is applied to a substrate, (2) a polymer film is formed from the coating material applied in stage (1), (3) a clearcoat material is applied to the resulting basecoat film, and then (4) the basecoat film is cured together with the clearcoat film, which comprises using in stage (1) a pigmented aqueous basecoat material which comprises at least one reaction product of the invention. All of the above observations relating to the reaction product of the invention and to the pigmented aqueous basecoat material are also valid in respect of the method of the invention. This is true more particularly also of all preferred, very preferred, and especially preferred features.

Said method is preferably used to produce multicoat color paint systems, effect paint systems, and color and effect paint systems.

The pigmented aqueous basecoat material used in accordance with the invention is commonly applied to metallic or plastics substrates that have been pretreated with surfacer or primer-surfacer. Said basecoat material may optionally also be applied directly to the plastics substrate.

Where a metallic substrate is to be coated, it is preferably further coated with an electrocoat system before the surfacer or primer-surfacer is applied.

Where a plastics substrate is being coated, it is preferably also pretreated before the surfacer or primer-surfacer is applied. The techniques most frequently employed for such pretreatment are those of flaming, plasma treatment, and corona discharge. Flaming is used with preference.

Application of the pigmented aqueous basecoat material of the invention to metallic substrates already coated, as described above, with cured electrocoat systems and/or surfacers may take place in the film thicknesses customary within the automobile industry, in the range, for example, of 5 to 100 micrometers, preferably 5 to 60 micrometers. This is done using spray application methods, for example compressed air spraying, airless spraying, high-speed rotation, electrostatic spray application (ESTA), alone or in conjunction with hot spray application, for example hot air spraying.

Following the application of the pigmented aqueous basecoat material, it can be dried by known methods. For example, (1-component) basecoat materials, which are preferred, can be flashed at room temperature for 1 to 60 minutes and subsequently dried, preferably at optionally slightly elevated temperatures of 30 to 90° C. Flashing and drying in the context of the present invention mean the evaporation of organic solvents and/or water, as a result of which the paint becomes drier but has not yet cured or not yet formed a fully crosslinked coating film.

Then a commercial clearcoat material is applied, by likewise common methods, the film thicknesses again being within the customary ranges, for example 5 to 100 micrometers.

After the clearcoat material has been applied, it can be flashed at room temperature for 1 to 60 minutes, for example, and optionally dried. The clearcoat material is then cured together with the applied pigmented basecoat material. In the course of these procedures, crosslinking reactions occur, for example, to produce on a substrate a multicoat color and/or effect paint system of the invention. Curing takes place preferably thermally at temperatures from 60 to 200° C. Thermally curing basecoat materials are preferably those which comprise as additional binder a polyurethane resin and as crosslinking agent an aminoplast resin or a blocked or nonblocked polyisocyanate, preferably an aminoplast resin. Among the aminoplast resins, melamine resins are preferred.

In one particular embodiment, the method for producing a multicoat paint system comprises the following steps:

producing a cured electrocoat film on the metallic substrate by electrophoretic application of an electrocoat material to the substrate and subsequent curing of the electrocoat material, producing (i) a basecoat film or (ii) a plurality of basecoat films directly following one another directly on the cured electrocoat film by (i) application of an aqueous basecoat material directly to the electrocoat film, or (ii) directly successive application of two or more basecoat materials to the electrocoat film, producing a clearcoat film directly on (i) the basecoat film or (ii) the uppermost basecoat film, by application of a clearcoat material directly to (i) one basecoat film or (ii) the uppermost basecoat film, where (i) one basecoat material or (ii) at least one of the basecoat materials is a basecoat material of the invention, joint curing of the basecoat film (i) or of the basecoat films (ii) and also of the clearcoat film.

In the latter embodiment, then, in comparison to the above-described standard methods, there is no application and separate curing of a commonplace surfacer. Instead, all of the films applied to the electrocoat film are cured jointly, thereby making the overall operation much more economical. Nevertheless, in this way, and particularly through the use of a basecoat material of the invention comprising a reaction product of the invention, multicoat paint systems are produced which have virtually no pinholes and hence are particularly visually outstanding. This is surprising in particular since with this method, within the concluding curing step, a particularly large quantity of organic solvents and/or water must escape from the system (since, indeed, there is no separate curing of a surfacer film), thereby greatly increasing the fundamental susceptibility to formation of pinholes.

The application of a coating material directly to a substrate or directly to a previously produced coating film is understood as follows: The respective coating material is applied in such a way that the coating film produced from it is disposed on the substrate (on the other coating film) and is in direct contact with the substrate (with the other coating film). Between coating film and substrate (other coating film), therefore, there is more particularly no other coat. Without the detail “direct”, the applied coating film, while disposed on the substrate (the other film), need not necessarily be present in direct contact. More particularly, further coats may be disposed between them. In the context of the present invention, therefore, the following is the case: In the absence of particularization as to “direct”, there is evidently no restriction to “direct”.

Plastics substrates are coated basically in the same way as metallic substrates. Here, however, in general, curing takes place at significantly lower temperatures, of 30 to 90° C. Preference is therefore given to the use of two-component clearcoat materials. Furthermore, in this context, preference is given to use of basecoat materials which comprise a polyurethane resin as binder, but no crosslinker.

The method of the invention can be used to paint metallic and nonmetallic substrates, more particularly plastics substrates, preferably automobile bodies or components thereof.

The method of the invention can be used further for dual finishing in OEM finishing. This means that a substrate which has been coated by means of the method of the invention is painted for a second time, likewise by means of the method of the invention.

The invention relates further to multicoat paint systems which are producible by the method described above. These multicoat paint systems are to be referred to below as multicoat paint systems of the invention.

All of the above observations relating to the reaction product of the invention and to the pigmented aqueous basecoat material are also valid in respect of said multicoat paint system and of the method of the invention. This is also true especially of all the preferred, more preferred and most preferred features.

The multicoat paint systems of the invention are preferably multicoat color paint systems, effect paint systems, and color and effect paint systems.

A further aspect of the invention relates to the method of the invention, wherein said substrate from stage (1) is a multicoat paint system having defects. This substrate/multicoat paint system, which possesses defects, is therefore an original finish, which is to be repaired or completely recoated.

The method of the invention is suitable accordingly for repairing defects on multicoat paint systems. Film defects are generally faults on and in the coating, usually named according to their shape or their appearance. The skilled person is aware of a host of possible kinds of such film defects. They are described for example in Rompp-Lexikon Lacke and Druckfarben, Georg Thieme Verlag, Stuttgart, New York, 1998, page 235, “Film defects”.

The multicoat paint systems produced by means of the method of the invention may likewise have such defects. In one preferred embodiment of the method of the invention, therefore, the substrate from stage (1) is a multicoat paint system of the invention which exhibits defects.

These multicoat paint systems are produced preferably on automobile bodies or parts thereof, by means of the method of the invention, identified above, in the context of automotive OEM finishing. Where such defects occur directly after OEM finishing has taken place, they are repaired immediately. The term “OEM automotive refinishing” is therefore also used. Where only small defects require repair, only the “spot” is repaired, and the entire body is not completely recoated (dual coating). The former process is called “spot repair”. The use of the method of the invention for remedying defects on multicoat paint systems (original finishes) of the invention in OEM automotive refinishing, therefore, is particularly preferred.

Where reference is made, in the context of the present invention, to the automotive refinish segment, in other words when the repair of defects is the topic, and the substrate specified is a multicoat paint system possessing defects, this of course means that this substrate/multicoat paint system with defects (original finish) is generally located on a plastic substrate or on a metallic substrate as described above.

So that the repaired site has no color difference from the rest of the original finish, it is preferred for the aqueous basecoat material used in stage (1) of the method of the invention for repairing defects to be the same as that which was used to produce the substrate/multicoat paint system with defects (original finish).

The observations above concerning the polymer of the invention and the aqueous pigmented basecoat material therefore are also valid for the use, under discussion, of the method of the invention for repairing defects on a multicoat paint system. This is also true in particular of all stated preferred, very preferred, and especially preferred features. It is additionally preferred for the multicoat paint systems of the invention that are to be repaired to be multicoat color paint systems, effect paint systems, and color and effect paint systems.

The above-described defects on the multicoat paint system of the invention can be repaired by means of the above-described method of the invention. For this purpose, the surface to be repaired on the multicoat paint system may initially be abraded. The abrading is preferably performed by partially sanding, or sanding off, only the basecoat and the clearcoat from the original finish, but not sanding off the primer layer and surfacer layer that are generally situated beneath them. In this way, during the refinish, there is no need in particular for renewed application of specialty primers and primer-surfacers. This form of abrading has become established especially in the OEM automotive refinishing segment, since here, in contrast to refinishing in a workshop, generally speaking, defects occur only in the basecoat and/or clearcoat region, but do not, in particular, occur in the region of the underlying surfacer and primer coats. Defects in the latter coats are more likely to be encountered in the workshop refinish sector. Examples include paint damage such as scratches, which are produced, for example, by mechanical effects and which often extend down to the substrate surface (metallic or plastic substrate).

After the abrading procedure, the pigmented aqueous basecoat material is applied to the defect site in the original finish by pneumatic atomization. After the pigmented aqueous basecoat material has been applied, it can be dried by known methods. For example, the basecoat material may be dried at room temperature for 1 to 60 minutes and subsequently dried at optionally slightly elevated temperatures of 30 to 80° C. Flashing and drying for the purposes of the present invention means evaporation of organic solvents and/or water, whereby the coating material is as yet not fully cured. For the purposes of the present invention it is preferred for the basecoat material to comprise a polyurethane resin as binder and an aminoplast resin, preferably a melamine resin, as crosslinking agent.

A commercial clearcoat material is subsequently applied, by techniques that are likewise commonplace. Following application of the clearcoat material, it may be flashed off at room temperature for 1 to 60 minutes, for example, and optionally dried. The clearcoat material is then cured together with the applied pigmented basecoat material.

In the case of so-called low-temperature baking, curing takes place preferably at temperatures of 20 to 90° C. Preference here is given to using two-component clearcoat materials. If, as described above, a polyurethane resin is used as further binder and an aminoplast resin is used as crosslinking agent, there is only slight crosslinking by the aminoplast resin in the basecoat film at these temperatures. Here, in addition to its function as a curing agent, the aminoplast resin also serves for plasticizing and may assist pigment wetting. Besides the aminoplast resins, nonblocked isocyanates may also be used. Depending on the nature of the isocyanate used, they crosslink at temperatures from as low as 20° C.

In the case of what is called high-temperature baking, curing is accomplished preferably at temperatures of 130 to 150° C. Here both one-component and two-component clearcoat materials are used. If, as described above, a polyurethane resin is used as further binder and an aminoplast resin is used as crosslinking agent, there is crosslinking by the aminoplast resin in the basecoat film at these temperatures.

For repairing defects on multicoat paint systems, in other words when the substrate is an original finish with defects, preferably a multicoat paint system of the invention that exhibits defects, the low-temperature baking is preferably employed.

A further aspect of the present invention is the use of the reaction product of the invention in pigmented aqueous basecoat materials for improving the stability with respect to optical defects, more particularly pinholes.

The quality of the stability with respect to pinholes may be determined in principle using the pinholing limit and also the number of pinholes. The pinholing limit and its determination may be described as follows: In the construction of a multicoat paint system, the film thickness of a basecoat film disposed beneath the clearcoat film is varied, and, moreover, this basecoat film is not baked separately, but is instead baked together with the clearcoat film. This coating film may be, for example, a film disposed directly on the electrocoat film and/or a film disposed directly beneath the clearcoat film. It follows from the introductory remarks that the tendency to form pinholes must increase as the thickness of this film goes up, since correspondingly larger amounts of air, of organic solvents and/or of water are required to escape from the film. The film thickness of this film at which pinholes become apparent is referred to as the pinholing limit. The higher the pinholing limit, the better, evidently, is the quality of the stability with respect to pinholes. The number of pinholes as well is of course an expression of the quality of the stability with respect to pinholes.

The invention is illustrated below using examples.

EXAMPLES Specification of Particular Components and Measurement Methods Polyester 1 (P1):

Prepared in accordance with example D, column 16, lines 37 to 59 of DE 4009858 A, using butyl glycol instead of butanol as organic solvent, the solvents present thus being butyl glycol and water. The corresponding dispersion of the polyester has a solids content of 60 wt %.

Determination of the Number-Average Molecular Weight:

The number-average molecular weight was determined by means of vapor pressure osmosis. Measurement was effected using a vapor pressure osmometer (model 10.00 from Knauer) on concentration series of the component under investigation in toluene at 50° C., with benzophenone as calibration substance for determination of the experimental calibration constant of the instrument employed (in accordance with E. Schroder, G. Müller, K.-F. Arndt, “Leitfaden der Polymer-charakterisierung” [Introduction to polymer characterization], Akademie-Verlag, Berlin, pp. 47-54, 1982, in which, though, benzil was used as calibration substance).

Production of Inventive Reaction Products (IR): IR1:

In a 4 l stainless steel reactor equipped with anchor stirrer, thermometer, and reflux condenser, 843.9 g of hydroxyl-terminated polybutadiene (Poly Bd® R20LM, from Cray Valley) with an OH number of 93.3 mg KOH/g and a number-average molecular weight as determined by means of vapor pressure osmosis of 1200 g/mol (0.703 mol) and 1394.8 g (12.219 mol) of ε-caprolactone (from BASF SE) were introduced under nitrogen and with stirring (OH number determination to DIN 53240). A sample was taken and an ε-caprolactone content of 62.1% (theoretical: 62.3%) was found by means of gas chromatography. The batch was then admixed with 11.4 g of tin octoate (Octa Soligen Tin 28, from Borchers), with stirring, and was heated to 150° C.

When the batch had been held at 150° C. for 4.5 hours, a further sample was taken and a free ε-caprolactone content of 0.1% (detection limit: 0.1%) was found by means of gas chromatography.

The batch was cooled to 120° C., diluted with 250 g of butyl glycol (from BASF SE), and discharged at room temperature.

This gave, after 48 hours, a polymer which is solid at room temperature, and can be melted at 80° C. prior to incorporation into coating materials.

Gas chromatography found an ε-caprolactone content of less than 0.1%.

The solids content of the resin is 89.8% (60 min at 130° C.)

Number-average molecular weight: 3100 g/mol.

IR2:

In a 4 l stainless steel reactor equipped with anchor stirrer, thermometer, and reflux condenser, 640.4 g of hydroxyl-terminated polybutadiene (Poly Bd® R20LM, from Cray Valley) with an OH number of 93.3 mg KOH/g and a number-average molecular weight as determined by means of vapor pressure osmosis of 1200 g/mol (0.534 mol) and 1601.0 g (14.025 mol) of ε-caprolactone (from BASF SE) were introduced under nitrogen and with stirring (OH number determination to DIN 53240). A sample was taken and an ε-caprolactone content of 71.2% (theoretical: 71.4%) was found by means of gas chromatography. The batch was then admixed with 8.6 g of tin octoate (Octa Soligen Tin 28, from Borchers), with stirring, and was heated to 150° C.

When the batch had been held at 150° C. for 5.5 hours, a further sample was taken and a free ε-caprolactone content of 0.1% (detection limit: 0.1%) was found by means of gas chromatography.

The batch was cooled to 120° C., diluted with 250 g of butyl glycol (from BASF SE), and discharged at room temperature.

This gave, after 48 hours, a polymer which is solid at room temperature, and can be melted at 80° C. prior to incorporation into coating materials.

Gas chromatography found an ε-caprolactone content of less than 0.1%.

The solids content of the resin is 89.5% (60 min at 130° C.)

Number-average molecular weight: 4000 g/mol.

IR3:

In a 4 l stainless steel reactor equipped with anchor stirrer, thermometer, and reflux condenser, 1147.9 g of hydroxyl-terminated polybutadiene (KRASOL® LBH-P 2000, from Cray Valley) with an OH number of 51.1 mg KOH/g and a number-average molecular weight as determined by means of vapor pressure osmosis of 2100 g/mol (0.547 mol) and 1093.2 g (9.577 mol) of ε-caprolactone (from BASF SE) were introduced under nitrogen and with stirring (OH number determination to DIN 53240). A sample was taken and an ε-caprolactone content of 47.3% (theoretical: 48.4%) was found by means of gas chromatography.

The batch was then admixed with 8.9 g of tin octoate (Octa Soligen Tin 28, from Borchers), with stirring, and was heated to 150° C.

When the batch had been held at 150° C. for 4.5 hours, a further sample was taken and a free ε-caprolactone content of 0.1% (detection limit: 0.1%) was found by means of gas chromatography.

The batch was cooled to 120° C., diluted with 250 g of butyl glycol (from BASF SE), and discharged at room temperature.

This gave, after 48 hours, a polymer which is solid at room temperature, and can be melted at 80° C. prior to incorporation into coating materials.

Gas chromatography found an ε-caprolactone content of less than 0.1%.

The solids content of the resin is 89.5% (60 min at 130° C.) Number-average molecular weight: 4020 g/mol.

IR4:

In a 4 l stainless steel reactor equipped with anchor stirrer, thermometer, and reflux condenser, 956.4 g of hydroxyl-terminated polybutadiene (KRASOL® HLB-P 2000, from Cray Valley) with an OH number of 46.6 mg KOH/g and a number-average molecular weight as determined by means of vapor pressure osmosis of 2410 g/mol (0.397 mol) and 787.1 g (6.896 mol) of ε-caprolactone (from BASF SE) were introduced under nitrogen and with stirring (OH number determination to DIN 53240). A sample was taken and an ε-caprolactone content of 44.9% (theoretical: 45.1%) was found by means of gas chromatography.

The batch was then admixed with 6.4 g of tin octoate (Octa Soligen Tin 28, from Borchers), with stirring, and was heated to 150° C.

When the batch had been held at 150° C. for 4.5 hours, a further sample was taken and a free ε-caprolactone content of 0.1% (detection limit: 0.1%) was found by means of gas chromatography.

The batch was cooled to 120° C., diluted with 750 g of butyl glycol (from BASF SE), and discharged at room temperature.

This gave, after 48 hours, a polymer which is solid at room temperature, and can be melted at 80° C. prior to incorporation into coating materials.

Gas chromatography found an ε-caprolactone content of less than 0.1%.

The solids content of the resin is 69.3% (60 min at 130° C.) Number-average molecular weight: 4170 g/mol.

Production of Aqueous Basecoat Materials Production of a Silver Comparative Waterborne Basecoat 1 (C1)

The components listed under “aqueous phase” in table A were stirred together in the order stated to form an aqueous mixture. In the next step an organic mixture was prepared from the components listed under “organic phase”. The organic mixture was added to the aqueous mixture. The combined mixture was then stirred for 10 minutes and adjusted, using deionized water and dimethylethanolamine, to a pH of 8 and to a spray viscosity of 58 mPas under a shearing load of 1000 s⁻¹ as measured with a rotary viscometer (Rheomat RM 180 instrument from Mettler-Toledo) at 23° C.

TABLE A Parts by Component weight Aqueous phase 3% Na-Mg phyllosilicate 26 solution Deionized water 13.6 Butyl glycol 2.8 Polyurethane-modified 4.5 polyacrylate; prepared as per page 7, line 55 to page 8, line 23 of DE 4437535 A 50% strength by weight 0.6 solution of Rheovis PU 1250 (BASF), rheological agent P1 3.2 TMDD (BASF) 0.3 melamine-formaldehyde 4.1 resin (Cymel 203 from Cytec) 10% dimethylethanolamine 0.3 in water polyurethane-based 20.4 graft copolymer; prepared as per page 19, line 44 to page 20, line 21 of DE 19948004 A, solids content adjusted to 32.5 wt % with deionized water TMDD (BASF) 1.6 3% strength by weight 3.9 aqueous Rheovis AS S130 solution; rheological agent, available from BASF Organic phase Mixture of two commercial 6.2 aluminum pigments, available from Altana-Eckart Butyl glycol 7.5 P1 5

Production of an Inventive Waterborne Basecoat Material 1 (I1)

To produce the inventive waterborne basecoat material I1, a paint was produced as for the production of the comparative waterborne basecoat material 1 (C1), using IR1, instead of the polyester P1, both in the aqueous phase and in the organic phase. Based on the solids fraction (nonvolatile fraction), the amount of IR1 used in I1 was the same as that of the polyester P1 used in C1. The different amounts of butyl glycol arising from the different solid contents of IR1 and of dispersion P1 were compensated in the formulation I1 by corresponding addition of butyl glycol.

Preparation of Inventive Basecoat Materials 2 to 4 (I2 to I14)

In the same way as for the preparation of I1, inventive basecoat materials I2 to I4 were prepared using the reaction products IR2 to IR4. Compensation for the different solids contents in relation to the polyester dispersion P1 took place again by corresponding addition of butyl glycol.

Table 1 shows again the polyesters and reaction products, and their proportions (based on the total amount of the waterborne basecoat materials), used in waterborne basecoat materials (WBM) C1 and I1 to I4, as an overview.

TABLE 1 Compositions of WBM C1 and I1 to I4 Reaction WBM [% by wt.] product C1 4.92 P1 I1 4.92 IR1 I2 4.92 IR2 I3 4.92 IR3 I4 4.92 IR4

Comparison Between Waterborne Basecoat Materials C1 and I1 to I4

To determine the pinholing limit and pinhole count, multicoat paint systems were produced by the following general method:

A cathodically electrocoated steel sheet of dimensions 30×50 cm was provided with an adhesive strip on one longitudinal edge, in order to be able to determine the film thickness differences after the coating. The particular waterborne basecoat material was applied electrostatically in wedge format. The resulting waterborne basecoat film was flashed off at room temperature for four minutes and subsequently intermediately dried in a forced air oven at 70° C. for 10 minutes. A customary two-component clearcoat material was applied electrostatically in a film thickness of 35 micrometers to the dried waterborne basecoat film. The resulting clearcoat film was flashed off at room temperature for 20 minutes. The waterborne basecoat film and the clearcoat film were then cured in a forced air oven at 140° C. for 20 minutes. Following visual evaluation of the pinholes in the resulting wedge-shaped multicoat paint system, the film thickness of the pinholing limit and the number of pinholes above this film thickness (in other words, the total number of pinholes on the painted sheet) were ascertained. The results can be found in table 2.

TABLE 2 Pinholing limit and pinhole count of multicoat paint systems produced using waterborne basecoat materials C1 and I1 to I4 Pinholing limit Pinhole WBM (micrometers) count C1 22 25 I1 26 7 I2 29 13 I3 27 6 I4 31 10

The results emphasize the fact that the use of the reaction products of the invention or of the waterborne basecoat materials of the invention significantly increases the pinholing limit by comparison with the comparative waterborne basecoat material C1, and at the same time reduces the pinhole count.

Production of a Silver Comparative Waterborne Basecoat Material 2 (C2)

The components listed under “aqueous phase” in table B were stirred together in the order stated to form an aqueous mixture. In the next step an organic mixture was prepared from the components listed under “organic phase”. The organic mixture was added to the aqueous mixture. The combined mixture was then stirred for 10 minutes and adjusted, using deionized water and dimethylethanolamine, to a pH of 8 and to a spray viscosity of 58 mPas under a shearing load of 1000 s⁻¹ as measured with a rotary viscometer (Rheomat RM 180 instrument from Mettler-Toledo) at 23° C.

TABLE B Parts by Component weight Aqueous phase 3% Na-Mg phyllosilicate 26 solution Deionized water 21.7 Butyl glycol 2.8 Polyurethane-modified 4.5 polyacrylate; prepared as per page 7, line 55 to page 8, line 23 of DE 4437535 A 50% strength by weight 0.6 solution of Rheovis PU 1250 (BASF), rheological agent P1 13.3 TMDD (BASF) 0.3 Melamine-formaldehyde 4.1 resin (Cymel 203 from Cytec) 10% dimethylethanolamine 0.3 in water polyurethane- based graft copolymer; 1.8 prepared as per page 19, line 44 to page 20, line 21 of DE 19948004 A, solids content adjusted to 32.5 wt % with deionized water TMDD (BASF) 1.6 3% strength by weight 3.9 aqueous Rheovis AS S130 solution; rheological agent, available from BASF Organic phase Mixture of two 6.2 commercial aluminum pigments, available from Altana-Eckart Butyl glycol 7.5 P1 5

Preparation of Inventive Waterborne Basecoat Materials 5 to 8 (I5 to I8)

In the same way as for the preparation of I1 to I4, inventive basecoat materials I5 to I8 were produced using the reaction products IR1 to IR4 on the basis of the comparative basecoat material C2 (table B) and with replacement of the polyester dispersion P1. Compensation for the different solids contents in relation to the polyester dispersion P1 took place again by corresponding addition of butyl glycol.

TABLE 3 Compositions of WBM C2 and I5 to I8 Reaction WBM [% by wt.] product C2 10.98 P1 I5 10.98 IR1 I6 10.98 IR2 I7 10.98 IR3 I8 10.98 IR4

Comparison Between Waterborne Basecoat Materials C2 and I5 to I8

As above for the multicoat paint systems produced using waterborne basecoat materials C1 and I1 to I4, multicoat paint systems were produced using aqueous basecoat materials C2 and I5 to I8. The evaluation in terms of pinholing limit and pinhole count also took place in the same way. The results can be found in table 4.

TABLE 4 Pinholing limit and pinhole count of multicoat paint systems produced using waterborne basecoat materials C2 and I5 to I8 Pinholing limit Pinhole WBM (micrometers) count C2 14 63 I5 19 15 I6 21 4 I7 23 17 I8 22 9

The results again emphasize the fact that the use of the reaction products of the invention or of the waterborne basecoat materials of the invention significantly increases the pinholing limit by comparison with the comparative waterborne basecoat material C2, and at the same time reduces the pinhole count. 

1: A pigmented aqueous basecoat material, comprising: a reaction product which is prepared by reaction of (a) at least one aliphatic linear polyester having two functional end groups (a.1), with (b) at least one diene polymer having two functional end groups (b.1), wherein at least one type of group (a.1) is reacted in a linking manner with at least one type of group (b.1), said components (a) and (b) are used in the reaction in a molar ratio of 2.3/0.7 to 1.7/1.6 and the resulting reaction product possesses a number-average molecular weight of 1000 to 15 000 g/mol. 2: The basecoat material as claimed in claim 1, wherein the diene polymer (b) is a polybutadiene having two functional end groups and a number-average molecular weight of 500 to 5000 g/mol. 3: The basecoat material as claimed in claim 2, wherein the diene polymer comprises two hydroxyl groups as functional end groups. 4: The basccoat material as claimed in claim 1, wherein components (a) and (b) are used in a molar ratio of 2.1/0.9 to 1.8/1.5. 5: The basecoat material as claimed in claim 1, wherein the reaction product is prepared by ring-opening reaction of an aliphatic lactone with a diene polymer comprising two hydroxyl end groups, the molar ratio of aliphatic lactone to diene polymer being from 2/1 to 50/1. 6: The basecoat material as claimed in claim 5, wherein the aliphatic lactone has the following formula (I):

in which R₁, R₂, R₃, and R₄, independently of one another, are H, C₁ to C₆ alkyl, C₃ to C₆ alkylene, or C₁ to C₆ alkoxy, and n and m independently of one another are an integer from 0 to
 6. 7: The basecoat material as claimed in claim 6, wherein the lactone is epsilon-caprolactone. 8: The basecoat material as claimed in claim 5, wherein the molar ratio of the aliphatic lactone to diene polymer is from 5/1 to 40/1. 9: The basecoat material as claimed in claim 1, wherein the sum total of the weight-percentage fractions, based on the total weight of the pigmented aqueous basecoat material, of all the reaction products is 0.1 to 30 wt %. 10: The pigmented aqueous basecoat material as claimed in claim 1, which comprises a polyurethane resin that is grafted with olefinically unsaturated monomers and that also comprises hydroxyl groups, and a melamine resin. 11: A reaction product prepared by reaction of (a) at least one aliphatic linear polyester having two functional end groups (a.1), with (b) at least one diene polymer having two functional end groups (b.1), wherein at least one type of group (a.1) is reacted in a linking manner with at least one type of group (b.1), said components (a) and (b) are used in the reaction in a molar ratio of 2.3/0.7 to 1.7/1.6 and the resulting reaction product possesses a number-average molecular weight of 1000 to 15 000 g/mol.
 12. (canceled) 13: A method for producing a multicoat paint system, comprising: (1) applying a pigmented aqueous basecoat material to a substrate, (2) forming a polymer film from the coating material applied in stage (1), (3) applying a clearcoat material to the resulting basecoat film, and then (4) curing the basecoat film together with the clearcoat film, wherein a pigmented aqueous basecoat material as claimed in claim 1 is used in stage (1). 14: The method as claimed in claim 13, wherein the substrate is a metallic substrate coated with a cured electrocoat film, and all of the films applied to the electrocoat film are cured jointly. 15: A multicoat paint system producible by the method as claimed in claim
 13. 16: The basecoat material as claimed in claim 6, wherein n+m is from 2 to
 6. 17: A method of improving stability of paint, the method comprising: adding a reaction product according to claim 11 to a paint that comprises a basecoat material. 